S3PS Heat Shrink Tube for Fiber Optic Dome Closure
|S3PS Heat Shrink Tube for Fiber Optic Dome Closure|
|Heavy wall cross-linked polyolefin||Operating temperature: -55~110ºC|
|Innovative locking mechanism, hermetically sealed||Shrink temperature: 125 ºC|
|Spiral polyamide adhesive, mirror like adhesive optional||Shrink ratio: 4:1|
|Excellent UV,corrosion,mechanical damage resistance|
|Thermo-chromatic paint changes color for proper installation|
|Reference||As supplied(mm)||After recovered(mm)||Standard length|
|UPM S3PS||ID min.||ID max.||WT nom.||mm|
|ID=Internal Diameter||WT=wall thickness|
|Hardness (Shore D)||ASTM D2671||≥ 45 HD|
|Tensile strength||ASTM D2671||≥19 MPa|
|Breakdown elongation||ASTM D2671||≥450%|
|Aging Tensile strength||ASTM D2671||≥18 MPa|
|158 ºC/168hrs Breakdown elongation||ASTM D2671||≥400%|
|Dielectric strength||ASTM D2671||≥15 KV/mm|
|Fungus resistance||ASTM G21||No incidence of fungal growth|
|UV resistance||ASTM G53||After 2000hrs elongation 360% min.|
|Water absorption||ASTM D570||23ºC/24hrs 0.2% max.|
|Low temperature flexibility(out layer)||ASTM D2671||-40ºC/4hrs No cracking|
|Low temperature flexibility(adhesive layer)||ASTM D2671||-20ºC/4hrs No cracking|
|Chemical resistance||Hydrochloric acid, concentration 0.1||23ºC/168hrs|
|Sulphuric acid, concentration 0.1|
|Sodium chloride,concentration 0.1|
|Sodium hydroxide, concentration 0.1|
|Sodium nitrate, concentration 0.1|
|Sodium sulphate, concentration 0.1|
|Chemical resistance||5%HCL/5%NaOH/5%NaCl||No corrosion; No leaking|
|Internal air pressure 60kPa/24hrs|
|Sealing||23ºC/100kPa duration 24hrs,or immersed in water for 15mins||Pass|
|Temperature cycling||10 temperature cycles from -40ºC to 60ºC,internal air||No leaking|
|pressure 60kPa, duration 2hrs at each temperature point|
|Thermal aging||60ºC/168hrs, internal air pressure 70kPa||Pass|
|Elongation||Pulling with D/45*1500N, internal air pressure 60kPa/24hrs||No leaking|
|Cable torsion||Subjecting the cable to 90 degree torsion loading,||No damage, No leaking|
|maximum torque:50Nm torsion distance 250mm,|
|internal air pressure 60kPa|
|Chemical attack||70% gasoline and 30%methylbenzene||No leaking|
|duration 168hrs, after 3 days internal|
|air pressure 100kPa|
|Ideal for aerial and underground applications, expecially in Fiber Optic Dome Splice Closure|
|Standard color : Black|
|Special colors (e.g. Clear) are available on request|
|Standard packaging is 150mm/pc|
|Special sizes and lengths are available on request|
|Please specify specification,color,quantity when ordering|
No adhesive at this end(8-10 mm) for locking the cable position
Accessories: Deviation Clip or branch-off clip+ Aluminum foil
Heat Shrinkable Cable Repair Branch off clip
|Heat Shrinkable Cable Repair Branch off clip|
|Casted by aluminum||Operating temperature: -25~90ºC|
|Coated by high temperature adhesive||Shrink temperature: 135ºC|
|Molded by EVA or PA hot melt||Halogen free|
|Four types: small, middle, big and super big||RoHS compliant|
|Small||S||65*28||EVA or PA|
|Medium||M||85*40||EVA or PA|
|Large||L||104*59||EVA or PA|
|Extra Large||XL||127*68||EVA or PA|
|Wide used in the heat-shrinkable tubing made the continuation of communication cable branch ,|
|can one divides into two, into three, then achieve a variety of cable perfect branch.|
|Standard color : Black|
|Standard packaging by pieces|
|Please specify specification, customized length, quantity when ordering|
In 2002, UPM was established in Dalian, China to manufacture heat shrink materials.
In 2003,UPM began selling products for shipyard and the high voltage switchgear cabinet industry.
In 2005, UPM became an approved global supplier to Siemens for High Voltage Switchgear .
In 2006, UPM began selling products to the automotive industry.
In 2007, UPM began producing heat shrink connectors, CE approved.
In 2008, UPM expanded the product line to include power cable accessories.
In 2009, UPM began producing products for the telecommunications industry.
In 2010, UPM expanded the production capability to include a variety of Moulded parts.
In 2011, UPM expanded their manufacturing expertise to include triple-layer co-extrusion products.
In 2012, UPM brought in more automated machineries used in extrusion, co-extrusion, expansion and splicing processes.
In 2013, UPM received UL486D certification for the S3(h ) and S3(nh) product lines.
In 2014, UPM began to sell triple layer tube for cable joint
In 2015, Co-extrusion tube with adhesive tube sold well.
In 2016, More products got UL 224 approval.
More news coming up... Let's shrink the world together. Let's choose Union Polymer.
Since its founding, UPM has distinguished itself with excellent product quality, comprehensive customized after-sales service, and timely delivery. Strong R&D and innovation are the core components for the sustainable growth of UPM. UPM's manufacturing plant is now 3 times larger than the original facility. The in-house 3MeV Dynamitron (3MeV E-Beam) equipment enables UPM to maintain quality control over the entire supply chain from formulation, compounding & granulation, extrusion, cross-linked radiation, expansion, adhesive application, slicing, printing, and packaging. New products are continuously being added to our product line to meet customer needs.